» home » heat shrink » high temperature heat shrink » pvdf heat shrink dimensions
|
Back to PVDF Heat Shrink
| 3/64" |
0.047 |
1.2 |
0.023 |
0.58 |
0.007 |
0.180 |
| 1/16" |
0.063 |
1.6 |
0.031 |
0.79 |
0.007 |
0.180 |
| 3/32" |
0.094 |
2.4 |
0.046 |
1.17 |
0.010 |
0.250 |
| 1/8" |
0.125 |
3.2 |
0.062 |
1.57 |
0.010 |
0.250 |
| 3/16" |
0.188 |
4.8 |
0.093 |
2.36 |
0.010 |
0.250 |
| 1/4" |
0.251 |
6.4 |
0.125 |
3.18 |
0.010 |
0.250 |
| 3/8" |
0.377 |
9.6 |
0.187 |
4.75 |
0.011 |
0.279 |
| 1/2" |
0.503 |
12.8 |
0.250 |
6.35 |
0.011 |
0.279 |
| 3/4" |
0.759 |
19.3 |
0.375 |
9.53 |
0.014 |
0.356 |
| 1" |
1.000 |
25.6 |
0.500 |
12.7 |
0.016 |
0.406 |
Back to PVDF Heat Shrink
| 3/64" |
0.047 |
1.2 |
0.023 |
0.58 |
0.008 |
0.203 |
| 1/16" |
0.063 |
1.6 |
0.031 |
0.79 |
0.008 |
0.203 |
| 3/32" |
0.094 |
2.4 |
0.046 |
1.17 |
0.009 |
0.229 |
| 1/8" |
0.125 |
3.2 |
0.062 |
1.57 |
0.009 |
0.229 |
| 3/16" |
0.188 |
4.8 |
0.093 |
2.36 |
0.009 |
0.229 |
| 1/4" |
0.251 |
6.4 |
0.125 |
3.18 |
0.011 |
0.279 |
| 3/8" |
0.377 |
9.6 |
0.187 |
4.75 |
0.011 |
0.279 |
| 1/2" |
0.503 |
12.8 |
0.250 |
6.35 |
0.011 |
0.279 |
| 3/4" |
0.759 |
19.3 |
0.375 |
9.53 |
0.014 |
0.356 |
| 1" |
1.000 |
25.6 |
0.500 |
12.7 |
0.016 |
0.406 |
| Physical |
Unaged |
Tensile strength |
ASTM D 638 |
Min. 5,000 psi |
| Elongation |
Min. 150% |
| Aged |
Tensile strength |
180° C / 168 hrs |
Min. 70% of the value of unaged specimens |
| Elongation |
Deformation |
150° C / 1 hr |
Max. 50% |
|
Heat shock |
300° C / 4 hrs |
No cracking, flowing or dripping |
|
Cold bend |
-55° C / 4 hrs |
No cracking |
|
Flexibility |
180° C / 168 hrs |
No cracking |
|
Secant modulus |
2% strain |
Min. 120,000 psi |
| Electrical |
Dielectric strength |
Room Temp. |
Min. 23.6kV / mm |
|
Volume resistivity |
- |
Min. 10 |
| Chemical |
Copper corrosion |
180° C / 168 hrs |
No corrosion |
|
Copper stability |
180° C / 168 hrs |
No sign of degradation |
|
Flammability |
VW-1 |
Pass |
|
|